Find the Mechanical and Chemical Properties of our Steel Coils
Our Steel Qualities DX51 S220GD DC01 DC01+ZE DX51+ZF DD11
Hot-dip galvanized steel
| Quality | Thickness/mm | Coating | Coating Quantity | Yield point Rp (MPa) | Tensile strength Rm (MPA) | Elongation A80 (in %) | C % | Si % | Mn % | P % | S % | Ti % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| DX51D | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | – | 270-500 | 22 | 0.18 | 0.5 | 1.2 | 0.12 | 0.045 | 0.3 |
| DX52D | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | 140-300 | 270-420 | 26 | 0.12 | 0.5 | 0.6 | 0.1 | 0.045 | 0.3 |
| DX53D | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | 140-260 | 270-380 | 30 | 0.12 | 0.5 | 0.6 | 0.1 | 0.045 | 0.3 |
| S220GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 220 | min. 300 | 20 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S250GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 250 | min. 330 | 19 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S280GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 280 | min. 360 | 18 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S320GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 320 | min. 390 | 17 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S350GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 350 | min. 420 | 16 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S390GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 390 | min. 460 | 16 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S420GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 420 | min. 480 | 15 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S450GD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | min. 450 | min. 510 | 14 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| HX260LAD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | 260-330 | 350-430 | 26 | 0.11 | 0.5 | 1 | 0.03 | 0.025 | 0.15 |
| HX300LAD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | 300-380 | 380-480 | 23 | 0.12 | 0.5 | 1.4 | 0.03 | 0.025 | 0.15 |
| HX340LAD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | 340-420 | 410-510 | 21 | 0.12 | 0.5 | 1.4 | 0.03 | 0.025 | 0.15 |
| HX380LAD | 0.30 – 4.00 | Z , ZF , ZM | Z50 – Z600 | 380-480 | 440-560 | 19 | 0.12 | 0.5 | 1.5 | 0.03 | 0.025 | 0.15 |
-Zinc (Z) -Galvanized
-Zinc-iron (ZF) -Galvannealed
-Zinc-magnesium (ZM) – Magnelis
ElectroGalvanized
| Quality | Thickness/mm | Yield point Rp (MPa) | Tensile strength Rm (MPA) | Elongation A80 (in %) | C % | Mn % | P % | S % |
|---|---|---|---|---|---|---|---|---|
| DC01+ZE | 0.30 – 3.00 | max. 280 | 270-410 | 28 | 0.12 | 0.6 | 0.045 | 0.045 |
| DC03+ZE | 0.30 – 3.00 | max. 240 | 270-370 | 34 | 0.1 | 0.45 | 0.035 | 0.035 |
| DC04+ZE | 0.30 – 3.00 | max. 220 | 270-350 | 37 | – | – | – | – |
| HC220B+ZE | 0.30 – 3.00 | 220-270 | 320-400 | 32 | – | – | – | – |
| HC260LA+ZE | 0.30 – 3.00 | 260-330 | 350-430 | 26 | – | – | – | – |
| HC300LA+ZE | 0.30 – 3.00 | 300-380 | 380-480 | 23 | – | – | – | – |
| HC340LA+ZE | 0.30 – 3.00 | 340-420 | 410-510 | 21 | – | – | – | – |
Cold Rolled
| Quality | Thickness/mm | Yield point Rp (MPa) | Tensile strength Rm (MPA) | Elongation A80 (in %) | C % | Si % | Mn % | P % | S % | Ti % |
|---|---|---|---|---|---|---|---|---|---|---|
| DC01 | 0.30 – 2.50 | ≤280 | 270 – 410 | 28 | 0,120 | – | 0.6 | 0.045 | 0.045 | – |
| DC03 | 0.30 – 2.50 | ≤240 | 270 – 370 | 34 | 0,100 | – | 0.45 | 0.035 | 0.035 | – |
| DC04 | 0.30 – 2.50 | ≤210 | 270 – 350 | 38 | 0,080 | – | 0.4 | 0.03 | 0.03 | – |
| DC01EK | 0.30 – 2.50 | ≤270 | 270 – 390 | 30 | 0,080 | – | 0.6 | 0.045 | 0.05 | – |
| HC260LA | 0.30 – 2.50 | 260 – 330 | 350 – 430 | 26 | 0.1 | 0.5 | 1 | 0.12 | 0.03 | 0.15 |
| HC300LA | 0.30 – 2.50 | 300 – 380 | 380 – 480 | 23 | 0.12 | 0.5 | 1.4 | 0.03 | 0.025 | 0.15 |
| HC340LA | 0.30 – 2.50 | 340 – 420 | 410 – 510 | 21 | 0.12 | 0.5 | 1.5 | 0.03 | 0.025 | 0.15 |
Hot Rolled & Pickled
| Quality | Thickness/mm | Yield point Rp (MPa) | Tensile strength Rm (MPA) | Elongation A80 (in %) | C % | Mn % | P % | S % | N % | Cu % | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| S235JR | 1.20 – 4.00 | 235 | 360 – 510 | 21 | ≤ 0,17 | ≤1,50 | ≤ 0,035 | ≤ 0,035 | ≤ 0,012 | ≤ 0,55 | |
| S275JR | 1.20 – 4.00 | 275 | 430 – 580 | 19 | ≤ 0,21 | ≤1,50 | ≤ 0,035 | ≤ 0,035 | ≤ 0,012 | ≤ 0,55 | |
| DD11 | 1.20 – 4.00 | 170 – 340 | ≤440 | 23 | ≤ 0,12 | ≤ 0,60 | ≤ 0,045 | ≤ 0,045 | – | – | |
| DD12 | 1.20 – 4.00 | 170 – 320 | ≤420 | 25 | ≤ 0,10 | ≤ 0,45 | ≤ 0,035 | ≤ 0,035 | – | – | |
| DD13 | 1.20 – 4.00 | 170 – 310 | ≤400 | 28 | ≤ 0,08 | ≤ 0,40 | ≤ 0,030 | ≤ 0,030 | – | – |
PrePainted (PPGI)
| Quality | Thickness/mm | Coating Quantity | Yield point Rp (MPa) | Tensile strength Rm (MPA) | Elongation A80 (in %) | C % | Si % | Mn % | P % | S % | Ti % |
|---|---|---|---|---|---|---|---|---|---|---|---|
| DX51D | 0.30 – 1.00 | Z50 – Z140 | – | 270-500 | 22 | 0.18 | 0.5 | 1.2 | 0.12 | 0.045 | 0.3 |
| DX52D | 0.30 – 1.00 | Z50 – Z140 | 140-300 | 270-420 | 26 | 0.12 | 0.5 | 0.6 | 0.1 | 0.045 | 0.3 |
| DX53D | 0.30 – 1.00 | Z50 – Z140 | 140-260 | 270-380 | 30 | 0.12 | 0.5 | 0.6 | 0.1 | 0.045 | 0.3 |
| S220GD | 0.30 – 1.00 | Z50 – Z140 | min. 220 | min. 300 | 20 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S250GD | 0.30 – 1.00 | Z50 – Z140 | min. 250 | min. 330 | 19 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S280GD | 0.30 – 1.00 | Z50 – Z140 | min. 280 | min. 360 | 18 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| S320GD | 0.30 – 1.00 | Z50 – Z140 | min. 320 | min. 390 | 17 | 0.2 | 0.6 | 1.7 | 0.1 | 0.045 | – |
| HX260LAD | 0.30 – 1.00 | Z50 – Z140 | 260-330 | 350-430 | 26 | 0.11 | 0.5 | 1 | 0.03 | 0.025 | 0.15 |